Introduction: Thermoplastic reflective road marking paint is made of thermoplastic petroleum resin, high-quality pigments and additives. Using it to mark line, the thermoplastic road marking paint has the advantages of quick drying, easy construction, good light reflection and long service life. Application: It can be used in asphalt or concrete road for long-acting marking. Technical Data: We can produce different standards of thermoplastic road marking paint, such as Chinese standard (JT/T280-04 and GB16311-09), BS standard, AASHTO standard and so on. The contents and raw materials are different with different standards. We can also produce according to customers’ non-standard customization.

Raw  Material	C5  Petroleum Resin, CaCO3, Glass Beads, DOP, PE, etc.
Gravity,  g/m3	2.1  g/ml
Color	white,  yellow,  etc.
Heating  Temperature	180℃-220℃
Softening  Point, ℃	110℃
Coating  Appearance	No  wrinkles, dots, blisters, cracks, fall-out & stick tyres
Drying  Time, min	Within  3 minutes
Compressive  Strength, MPa	26
Abrasive  Resistance, mg	42
Water  Resistance	Great(in  water for 24 hours)
Alkali  Resistance	Great(in  saturated solution of calcium hydroxide for 24 hours)
Glass  Beads, %	30~40%
Fluidity,  s	40s
Coating  Resisitance	Resist  -10℃ for 4 hours
Heat  Resistance	Under  0℃-2℃ for 4 hours

Package & Use:

Package	25kg/bag,  by plastic woven bag. One ' container can load Max. 25 tons.
Storage	dry, cool,  avoid direct sunlight
Expiration  date	365  days
Theoretical  spray rate	4-5kg/㎡

Features: 1. Cohesiveness Specific formula, of good cohesiveness with road, pre-mark with our company’s dedicated primer (especially for concrete base) will strengthen the cohesiveness. 2. Anti-slipperiness Our paint has anti-slipping material. On condition of good flowability, the anti-slipping material can ensure good anti-slipperiness and maximize the traffic safety. 3. Reflective effect According to the settling rate of the glass beads, properly choose stable refractive and high quality coating type glass beads with different particle ratio. Mix them evenly inside the paint and dispense mixed type glass beads when executing will ensure new and old marking always to be in high reflection. 4. Dry fast Use different formula to produce the paint according to temperature, humidity and roadbed condition when executing, ensure fast drying speed and antifouling property of the marking. 5. Stability Choose excellent light and heat stability raw material ratio, add ultraviolet-proof additives at the same time, to make sure the long-acting color and luster even under strong sunshine. 6. Anti hair-cracking Hair-cracking of the marking is a technical problem in road marking material industry home and abroad. After long-term research and by way of adding high temperature resistance lipid material and functional filler, our company completely solved the hair-cracking problem during executing.Hot melt scribing coating adopts glass bead primer and petroleum resin hot melt coating. Heat the coating in the hot-melt machine, control the melting temperature between 18 ° C and 220 ° C, and fully stir for about 10 minutes before coating. Mark and measure the position according to the position and figure indicated in the design drawing, and then apply the primer on the way of marking. Hot melt coating can be applied only after the primer is dry. Reflective glass beads are spread while marking to increase night identification.